| 廠家(產地) | EASTAR | 牌號 | PC1451 | 加工級別 | 注塑級,擠出級 |
| 特性級別 |
阻燃級,增韌級,增強級,耐低溫,耐候,抗化學性 ,高流動,高抗沖,高結晶（HCPP） |
用途級別 | 家電部件,薄壁制品 | 銷售方式 | 自產自銷 |
|
PC1451材料 耐寒超高韌性，共聚物，可加工性良好，流動性中等，易脫模，低溫延展性,
TYPICAL PROPERTIES?(1) |
||||
| MECHANICAL | Value | Unit | Standard | |
| Tensile Stress, yld, Type I, 50 mm/min | 560 | kgf/cm2 | ASTM D 638 | |
| Tensile Stress, brk, Type I, 50 mm/min | 510 | kgf/cm2 | ASTM D 638 | |
| Tensile Strain, yld, Type I, 50 mm/min | 6 | % | ASTM D 638 | |
| Tensile Strain, brk, Type I, 50 mm/min | 98 | % | ASTM D 638 | |
| Tensile Modulus, 50 mm/min | 20500 | kgf/cm2 | ASTM D 638 | |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 940 | kgf/cm2 | ASTM D 790 | |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 22700 | kgf/cm2 | ASTM D 790 | |
| Hardness, Rockwell L | 89 | - | ASTM D 785 | |
| Hardness, Rockwell R | 121 | - | ASTM D 785 | |
| Tensile Stress, yield, 50 mm/min | 57 | MPa | ISO 527 | |
| Tensile Stress, break, 50 mm/min | 60 | MPa | ISO 527 | |
| Tensile Strain, yield, 50 mm/min | 6 | % | ISO 527 | |
| Tensile Strain, break, 50 mm/min | 120 | % | ISO 527 | |
| Tensile Modulus, 1 mm/min | 2150 | MPa | ISO 527 | |
| Flexural Stress, yield, 2 mm/min | 85 | MPa | ISO 178 | |
| Flexural Modulus, 2 mm/min | 2250 | MPa | ISO 178 | |
| IMPACT | Value | Unit | Standard | |
| Izod Impact, notched, 23°C | 88 | cm-kgf/cm | ASTM D 256 | |
| Izod Impact, notched, -30°C | 78 | cm-kgf/cm | ASTM D 256 | |
| Instrumented Impact Total Energy, 23°C | 714 | cm-kgf | ASTM D 3763 | |
| Izod Impact, unnotched 80*10*3 +23°C | NB | kJ/m2 | ISO 180/1U | |
| Izod Impact, unnotched 80*10*3 -30°C | NB | kJ/m2 | ISO 180/1U | |
| Izod Impact, notched 80*10*3 +23°C | 70 | kJ/m2 | ISO 180/1A | |
| Izod Impact, notched 80*10*3 -30°C | 60 | kJ/m2 | ISO 180/1A | |
| Charpy 23°C , V-notch Edgew 80*10*3 sp=62mm | 70 | kJ/m2 | ISO 179/1eA | |
| Charpy -30°C , V-notch Edgew 80*10*3 sp=62mm | 65 | kJ/m2 | ISO 179/1eA | |
| Charpy 23°C , Unnotch Edgew 80*10*3 sp=62mm | NB | kJ/m2 | ISO 179/1eU | |
| Charpy -30°C , Unnotch Edgew 80*10*3 sp=62mm | NB | kJ/m2 | ISO 179/1eU | |
| THERMAL | Value | Unit | Standard | |
| Vicat Softening Temp, Rate B/50 | 145 | °C | ASTM D 1525 | |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 139 | °C | ASTM D 648 | |
| HDT, 1.82 MPa, 3.2mm, unannealed | 124 | °C | ASTM D 648 | |
| CTE, -40°C to 40°C , flow | 6.96E-05 | 1/°C | ASTM E 831 | |
| CTE, -40°C to 40°C , xflow | 7.47E-05 | 1/°C | ASTM E 831 | |
| CTE, 23°C to 80°C , flow | 7.2E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 80°C , xflow | 7.2E-05 | 1/°C | ISO 11359-2 | |
| Vicat Softening Temp, Rate B/50 | 145 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/120 | 146 | °C | ISO 306 | |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 140 | °C | ISO 75/Be | |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 128 | °C | ISO 75/Ae | |
| Relative Temp Index, Elec | 130 | °C | UL 746B | |
| Relative Temp Index, Mech w/impact | 120 | °C | UL 746B | |
| Relative Temp Index, Mech w/o impact | 125 | °C | UL 746B | |
| PHYSICAL | Value | Unit | Standard | |
| Specific Gravity | 1.18 | - | ASTM D 792 | |
| Mold Shrinkage, flow, 3.2 mm | 0.4 - 0.8 | % | EASTAR?Method | |
| Mold Shrinkage, xflow, 3.2 mm | 0.4 - 0.8 | % | EASTAR Method | |
| Melt Flow Rate, 300°C /1.2 kgf | 10 | g/10 min | ASTM D 1238 | |
| Density | 1.19 | g/cm2 | ISO 1183 | |
| Water Absorption, (23°C /sat) | 0.35 | % | ISO 62 | |
| Moisture Absorption (23°C / 50% RH) | 0.15 | % | ISO 62 | |
| Melt Volume Rate, MVR at 300°C /1.2 kg | 9 | cm3/10 min | ISO 1133 | |
| ELECTRICAL | Value | Unit | Standard | |
| Volume Resistivity | >1.E+15 | Ohm-cm | ASTM D 257 | |
| Surface Resistivity | >1.E+15 | Ohm | ASTM D 257 | |
| Dielectric Strength, in oil, 0.8 mm | 16.2 | kV/mm | ASTM D 149 | |
| Relative Permittivity, 100 Hz | 2.68 | - | ASTM D 150 | |
| Relative Permittivity, 1 MHz | 2.64 | - | ASTM D 150 | |
| Dissipation Factor, 100 Hz | 0.0012 | - | ASTM D 150 | |
| Dissipation Factor, 1 MHz | 0.0093 | - | ASTM D 150 | |
| FLAME CHARACTERISTICS | Value | Unit | Standard | |
| UL Recognized, 94HB Flame Class Rating (3) | 0.4 | mm | UL 94 | |
| Glow Wire Flammability Index 850°C , passes at | 0.8 | mm | IEC 60695-2-12 | |
| Glow Wire Flammability Index 960°C , passes at | 1 | mm | IEC 60695-2-12 | |
| Glow Wire Ignitability Temperature, 1.0 mm | 875 | °C | IEC 60695-2-13 | |
| Glow Wire Ignitability Temperature, 3.0 mm | 875 | °C | IEC 60695-2-13 | |
| Processing |
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 120 | °C |
| Drying Time | 3 - 4 | hrs |
| Drying Time (Cumulative) | 48 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 295 - 315 | °C |
| Nozzle Temperature | 290 - 310 | °C |
| Front - Zone 3 Temperature | 295 - 315 | °C |
| Middle - Zone 2 Temperature | 280 - 305 | °C |
| Rear - Zone 1 Temperature | 215 - 295 | °C |
| Mold Temperature | 70 - 95 | °C |
| Back Pressure | 0.3 - 0.7 | MPa |
| Screw Speed | 40 - 70 | rpm |
| Shot to Cylinder Size | 40 - 60 | % |
| Vent Depth | 0.025 - 0.076 | mm |
東積架新材料科技不僅是專業的熱塑性彈性體及工程材料原料供應商，亦注重技術支持及全方位的解決方案，提供從設計選材、模具設計、成型加工等系列幫助，亦可為客戶量身定制各特殊性能之材料，進而協助客戶提高產品竟爭力!
歡迎來電咨詢！
東積架實業香港有限公司
EASTAR Industry (HK)Co.,Limited
深圳市東積架新材料科技有限公司
Shenzhen EASTAR New Materials Technology Co,.LTD
貴賓熱線：唐生13430746085
免責聲明：（1）以上所展示的信息由企業自行提供，內容的真實性、準確性和合法性由發布企業負責，環球塑化網對此不承擔任何保證責任。我們原則上建議您優先選擇“塑企通”會員合作! （2）同時我們鄭重提醒各位買/賣家，交易前請詳細核實對方身份，切勿隨意打款或發貨，謹防上當受騙。如發現虛假信息，請向環球塑化網舉報。
簡繁切換